Large-Particle Aluminum Diethylphosphinate Flame Retardant
FR-ADP04 is a flame retardant specifically designed for use in engineering plastics such as PBT, PET, and polyamide. Its unique particle size process helps prevent decomposition during polymer granulation, maintaining material properties and color stability. This flame retardant is ideal for both glass fibre reinforced and non-reinforced grades of PBT and PET, offering excellent physical and electrical properties.
| Item | Value |
| Appliccation | pbt，pet，tpe |
| Shape | White Powder |
| Water/Moisture | 0.2% |
| Decomposition Temperature | 360℃ |
| Average Particle Size (D50) | 25μm |
| Phosphorus Content | 23.5% (w/w) |
| Density | 1.35g/cm3 |
| Bulk Density | 550g/cm3 |
Large particle size
Retains effectiveness under elevated temperatures.
High temperature resistance
In Glass Fiber Reinforced PBT:
To achieve a UL 94 V-0 classification at 1.6 mm thickness, a typical dosage of 10% FR-ADP04 combined with 5% nitrogen-based flame retardant is recommended. Dosage may vary depending on the specific formula and processing conditions.
In Glass Fiber Reinforced PA6 and Other Composites:
For a UL 94 V-0 classification at 0.8 mm thickness, a dose of 12% FR-ADP04 combined with 6% nitrogen-based flame retardant is typically sufficient.
Packaged in a paper-plastic composite bag and lined with a plastic bag. 25 kg per package.
The product must be sealed, kept dry, dust-free, and cool
Large-Particle Aluminum Diethylphosphinate Flame Retardant
FR-ADP04 is a flame retardant specifically designed for use in engineering plastics such as PBT, PET, and polyamide. Its unique particle size process helps prevent decomposition during polymer granulation, maintaining material properties and color stability. This flame retardant is ideal for both glass fibre reinforced and non-reinforced grades of PBT and PET, offering excellent physical and electrical properties.
| Item | Value |
| Appliccation | pbt，pet，tpe |
| Shape | White Powder |
| Water/Moisture | 0.2% |
| Decomposition Temperature | 360℃ |
| Average Particle Size (D50) | 25μm |
| Phosphorus Content | 23.5% (w/w) |
| Density | 1.35g/cm3 |
| Bulk Density | 550g/cm3 |
Large particle size
Retains effectiveness under elevated temperatures.
High temperature resistance
In Glass Fiber Reinforced PBT:
To achieve a UL 94 V-0 classification at 1.6 mm thickness, a typical dosage of 10% FR-ADP04 combined with 5% nitrogen-based flame retardant is recommended. Dosage may vary depending on the specific formula and processing conditions.
In Glass Fiber Reinforced PA6 and Other Composites:
For a UL 94 V-0 classification at 0.8 mm thickness, a dose of 12% FR-ADP04 combined with 6% nitrogen-based flame retardant is typically sufficient.
Packaged in a paper-plastic composite bag and lined with a plastic bag. 25 kg per package.
The product must be sealed, kept dry, dust-free, and cool